关西油漆_无机富锌底漆2000_中远关西涂料

SD ZINC PRIMER 2000 无机富锌底漆2000

PRODUCT DESCRIPTION

产品简介

A self-curing inorganic zinc coating based on alkyl silicate binder

烷基硅酸酯为基料的自干型无机富锌涂料

RECOMMENDED USE

用途

Compatible with blasted steel surfaces and inorganic zinc shop-primed surfaces

适用于预处理后的钢材及无机富锌车间底漆表面

COMPLIED STANDARDS

符合标准

Complies with ISO 12944-5、SSPC PAINT 20、HG/T 3668-2009

符合ISO 12944-5、SSPC PAINT 20、HG/T 3668-2009 富锌底漆中的成分要求

FEATURES

产品特性

Remarkable corrosion resistance

极好的防腐性能

Outstanding resistance to impact, mechanical abrasion and organic solvent

优良的耐冲击、耐磨损和耐有机溶剂性能

Excellent initial hardness

极好的初始硬度

High-build applicability

极好的厚涂施工性能

Remarkable heat resistance and less scorch by heat treatment

优良的耐热性，热处理烧损少

PHYSICALPROPERTIES

基本数据

Color

颜色

Volume Solids

体积固体份

VOC

挥发性有机化合物含量

Flash Point

闪点

Film thickness

涂装膜厚

Theoretical Coverage

理论涂布率

Grey

灰色

60%

402g/L，accord with EU Dircrtive2004/42/EC，subcategory j

402g/L，符合欧盟溶剂排放指令2004/42/EC，j 子类别

Greater than 19℃

19℃以上

Dry : 60-75 microns/coat Wet : 100-125microns/coat

干膜: 60-75 微米/道湿膜:100-125 微米/道

0.373kg/m2/75microns

0.373 千克/平方米/75 微米

Practical coverage depending on surface conditions, environment, applications, etc.

实际涂布率与表面处理, 外界环境, 施工方法等多种因素有关。

APPLICATION

施工

Application Temperature

施工温度

Mixing

混合

Mixing Ratio

混合比例

Pot Life

混合使用期

5℃-40℃

Add powder to liquid first, then mix thoroughly with power agitator

将粉末加入液体，使用动力工具搅拌均匀

Liquid/Powder=20/86(by weight)

液体粉末=20/86（重量比）

5℃ 10℃ 20℃ 30℃

8hrs 7hrs 6hrs 5hrs

Application Methods

施工方法

Thinner

稀释剂

Drying time &

Overcoating interval

干燥时间&涂装间隔

Applied Substrates

适用底材

Typical topcoat

适用上涂

Airless spray, air spray

无气喷涂、空气喷涂

Airless spray 无气喷涂

Nozzle tip 喷嘴尺寸0.43mm-0.5

---